Test report of NIJ Level IIIA bulletproof helmet
Summary of NIJ Level IIIA bulletproof helmet Test Sample PASGT bulletproof helmet – PEIIIA Test Standard NIJ 0106.01 IIIA Test Ammunition .44 Magnum SWCGC 240gr x 4 shots Test By H.P. White Laboratory, Inc. (USA) Test Time 2009 Test Result All passed testing for NIJ IIIA Test report of NIJ Level IIIA bulletproof helmet
Test report of NIJ Level IV bulletproof vest/plate – Al2O3
Summary of NIJ level IV bulletproof vest/plate – Aluminum Oxide Test Sample 25x30cm PAIV-ICW/IIIA plate ~2.47kg/pc (made from PE + Aluminum Oxide Ceramic) tested in conjunction with IIIA vest Test Standard NIJ 0101.06 level IV Test Ammunition 7.62mm armor-piercing cartridge type 53 x 6 shots Test By China Ordnance Equipment Test Center Test Time 2015 Test Result All passed testing for NIJ 0101.06 level IV Test report of NIJ level IV bulletproof vest/plate – Aluminum Oxide ICW
Test report of NIJ Level IV bulletproof plate – Al2O3
Summary of NIJ level IV bulletproof plate – Aluminum Oxide Test Sample 25x30cm PAIV-ICW plate ~2.82kg/pc (made from PE + Aluminum Oxide Ceramic) tested stand alone Test Standard NIJ 0101.06 level IV Test Ammunition 7.62mm armor-piercing cartridge type 53 x 4 shots Test By China Ordnance Equipment Test Center Test Time 2015 Test Result All passed testing for NIJ 0101.06 level IV Test report of NIJ level IV bulletproof plate – Aluminum Oxide
Test report of NIJ Level IV bulletproof vest/plate – SiC
Summary of NIJ level IV bulletproof vest/plate – silicon carbide Test Sample 25x30cm PS-IV-ICW plate ~2.67kg/pc (made from PE + Silicon Carbide Ceramic) tested in conjunction with IIIA 9mm vest Test Standard NIJ 0101.06 level IV Test Ammunition 7.62mm armor-piercing cartridge type 53 x 3 shots Test By China Ordnance Equipment Test Center Test Time 2012 Test Result All passed testing for NIJ 0101.06 level IV Test report of NIJ level IV bulletproof vest/plate – silicon carbide
Test report of 400D UHMWPE Fiber in 2009
The test sample is 400D/240F UHMWPE fiber in original white color and test by CTTC in 2009 and the tenacity was 35.1cN/dtex. Tested Item Result Standard Linear Density 418.2dtex ISO 2060-1994 Diameter 18.12Nano ISO 137-1975 Breaking Tenacity 35.1cN/dtex ISO 2062-1993 CV of breaking tenacity 6.36% Breaking elongation 3.07% CV of breaking elongation 7.73% *The test results are transferred from below Chinese version. Part view of UHMWPE fiber test report – 400D/240F
Test report of 200D UHMWPE Fiber in 2008
The test sample is 200D/60F UHMWPE fiber in original white color and test by CTTC in 2008 and the tenacity was 31.7cN/dtex. Tested Item Result Standard Linear Density 222dtex Breaking Tenacity 31.7cN/dtex ISO 2062-1993 CV of breaking tenacity 6.57% Breaking elongation 3.18% CV of breaking elongation 8.55% *The test results are transferred from below Chinese version. Part view of UHMWPE fiber test report – 200D/60F
Test report of 800D UHMWPE Fiber in 2014
The test sample is 800D/480F UHMWPE fiber in original white color and test by CTTC in 2014 and the tenacity was 28.6cN/dtex. Tested Item Result Standard Linear Density 907.3dtex GB/T 19975-2005 Breaking Tenacity 28.6cN/dtex GB/T 19975-2005 CV of breaking tenacity 6.41% GB/T 19975-2005 Breaking elongation 2.94% GB/T 19975-2005 CV of breaking elongation 9.34% GB/T 19975-2005 Initial Modulus 1297cN/dtex GB/T 19975-2005 *The test results are transferred from below Chinese version. Part view of UHMWPE fiber test report – 800D/480F
Test report of 800D UHMWPE Fiber in 2018
The test sample is 800D/480F UHMWPE fiber in original white color and test by CTTC in 2018 and the tenacity was 35.5cN/dtex. Tested Item Result Standard Linear Density 955.9dtex GB/T 19975-2005 Breaking Tenacity 35.5cN/dtex GB/T 19975-2005 CV of breaking tenacity 7.76% GB/T 19975-2005 Breaking elongation 3.00% GB/T 19975-2005 CV of breaking elongation 8.72% GB/T 19975-2005 Initial Modulus 1620cN/dtex GB/T 19975-2005 *The test results are transferred from below Chinese version. Part view of UHMWPE fiber test report – 800D/480F
Test report of 800D UHMWPE Fiber in 2019
The test sample is 800D/480F UHMWPE fiber in original white color and test by CTTC in 2019 and the tenacity was 36.7cN/dtex. Tested Item Result Standard Linear Density 891.6dtex GB/T 19975-2005 Breaking Tenacity 36.7cN/dtex GB/T 19975-2005 CV of breaking tenacity 5.46% GB/T 19975-2005 Breaking elongation 3.25% GB/T 19975-2005 CV of breaking elongation 5.84% GB/T 19975-2005 Initial Modulus 1490cN/dtex GB/T 19975-2005 Oil Content 0.05% GB/T 6504-2008 *The test results are transferred from below Chinese version. Part view of UHMWPE fiber test report – 800D/480F
Test report of 1600D UHMWPE Fiber in 2008
The test sample is 1600D/480F UHMWPE fiber in original white color and test by CTTC in 2008 and the tenacity was 27.7cN/dtex. Tested Item Result Standard Breaking Tenacity 27.7cN/dtex ISO 2062-1993 CV of breaking tenacity 5.30% Breaking elongation 2.40% CV of breaking elongation 8.52% *The test results are transferred from below Chinese version. Part view of UHMWPE fiber test report – 1600D/480F
Test report of 1600D UHMWPE Fiber in 2014
The test sample is 1600D/960F UHMWPE fiber in original white color and test by CTTC in 2014 and the tenacity was 31cN/dtex. Tested Item Result Standard Linear Density 1742.2dtex GB/T 19975-2005 Breaking Tenacity 31cN/dtex GB/T 19975-2005 CV of breaking tenacity 5.99% GB/T 19975-2005 Breaking elongation 3.20% GB/T 19975-2005 CV of breaking elongation 6.81% GB/T 19975-2005 Melting Point 140 degrees FZ/T 01057.6-2007 *The test results are transferred from below Chinese version. Part view of UHMWPE fiber test report – 1600D/960F
Test report of 1600D UHMWPE Fiber in 2019
The test sample is 1600D/480F UHMWPE fiber in original white color and test by CTTC in 2019 and the tenacity was 32cN/dtex. Tested Item Result Standard Linear Density 1772.8dtex GB/T 19975-2005 Breaking Tenacity 32cN/dtex GB/T 19975-2005 CV of breaking tenacity 2.78% GB/T 19975-2005 Breaking elongation 3.36% GB/T 19975-2005 CV of breaking elongation 6.88% GB/T 19975-2005 Initial Modulus 1440cN/dtex GB/T 19975-2005 *The test results are transferred from below Chinese version. Part view of UHMWPE fiber test report – 1600D/480F